W. NR. 1.1730
0 CZK
Characteristics
Carbon tool steel characterized by adequate hardness of hardening layer, high toughness and very significant insensitivity to hardening cracks. Further the steel is characterized by good ductility at the heat and good workability in the annealed state.
Suitability
For locksmith and assembly tools, tools for woodworking, hardened components of molds, e.g. base plates, cases, columns, stops, suspension components and products etc. Further the steel is appropriate for agricultural, blacksmith and bricklayer tools.
Chemical composition of steel W.Nr. 1.1730
| Steel grade | Chemical composition in % | Hardness in the state | |||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| soft-annealed | heat-treated | ||||||||||||
| C | Mn | Si | Cr | W | Mo | V | Ni max | Co | P max. | S max. | HB max. | HRC min. | |
| DIN C45W | 0,40-0,50 | 0,60-0,80 | 0,15-0,40 | 0,035 | 0,035 | 190 | 57 | ||||||
| ČSN 19 083 | 0,40-0,50 | 0,60-0,80 | 0,15-0,40 | 0,035 | 0,035 | 190 | 56 | ||||||
Heat treatment of steel W.Nr. 1.1730
| Way | Temperature [°C] | Procedure | |
|---|---|---|---|
| Forging | 1050-800 | Cool slowly in calm air or better e.g. in dry ash or other thermally-insulated material | |
| Normalization | 840-860 | Cool in air | |
| Soft annealing | 680-710 | Warm few hours (according to the size of object). Mostly four hours are enough and cool slowly in the furnace | |
| Annealing to lower tension | 600-650 | Warm 1 to 2 hours and cool slowly in the furnace | |
| Hardening | in water | 790-820 | Big and simple objects |
| in oil | 800-830 | Thin cross-sections of thickness up to 5 mm | |
| Tempering | 180-300 | Cool in air or water, the degree of tempering is set by hardness and toughness of instrument according to the tempering chartPoznámka | |
Note
- Cross-sections thicker than 5 mm have a hardening irregular layer and are softer on the surface at hardening into oil.
- After hardening into oil the hardness of about 50 HRC is reached.Tabulka popouštěcích hodnot v závislosti na tvrdosti
Chart of tempering values depending on the hardness
| °C | 100 | 200 | 300 | 350 |
|---|---|---|---|---|
| HRC | 58 | 55 | 48 | 44 |
Graph
Product range
Round bars: D20 - D615
Metal sheets: s.10 - s.200
Blocks: 510x1600
We will deliver any semi-finished products from the above mentioned dimensions. Other dimensions, except for given stock supplies, have to be consulted with us.