W. NR. 1.2083 ESU
CZK 0
Characteristics
Resistant to the corrosion, Martensite steel with the high content of chrome. The steel has good resistance to the wear, good workability and due to the ESU method also excellent polishability.
Suitability
Molds for pressing of chemically-aggressive plastic substances etc.
Chemical composition of steel W.Nr. 1.2083ESU
| Steel grade | Chemical composition in % | Hardness in state | |||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| soft-annealed | heat-treated | ||||||||||||
| C | Mn | Si | Cr | W | Mo | V | Ni max | Co | P max. | S max. | HB max. | HRC min. | |
| DIN X42Cr13 | 0,38-0,45 | 1,00 | 1,00 | 12,50-13,50 | 0,030 | 0,030 | 230 | 56 | |||||
| ČSN není | |||||||||||||
Heat treatment of steel W.Nr. 1.2083ESU
| Way | Temperature [°C] | Procedure | |
|---|---|---|---|
| Forging | 1000-1050 | Cool slowly in calm air or better e.g. in dry ash or other thermally-insulated material | |
| Normalization | 790-810 | Cool in air | |
| Soft annealing | 750-800 | Warm few hours (according to the size of object), mostly four hours are enough and cool slowly in the furnace | |
| Annealing to lower tension | 600-650 | Warm 1 to 2 hours and cool slowly in the furnace | |
| Hardening | 1000-1050 | Cool in oil or hot bath, the degree of tempering is set by hardness and toughness of instrument according to the tempering chart | |
| Tempering | 150-300 | For cold work | |
| 400-600 | For hot work | ||
Note
Chart of tempering values depending on the hardness:
| °C | 100 | 200 | 300 | 400 | 500 | 600 |
|---|---|---|---|---|---|---|
| HRC | 56 | 55 | 52 | 51 | 52 | 40 |
Graph
Product range
Bars: D25 - D202
Blocks: 460x810
We will deliver any semi-finished products from the above mentioned dimensions. Other dimensions, except for given stock supplies, have to be consulted with us.